Titanium impregnated silica-chromium catalysts

ABSTRACT

In accordance with a first embodiment of this invention, a silica xerogel is aqueously impregnated with a titanium compound which is resistant to hydrolysis. In accordance with a second embodiment of this invention, a silica hydrogel containing a titanium compound resistant to hydrolysis is dried. In this embodiment, the hydrogel preferably also contains a pore preserving agent. This invention makes possible the use of aqueous impregnation of titanium and conventional drying techniques to give a catalyst having characteristics associated with azeotrope dried silica-titanium coprecipitated catalyst. The catalysts of this invention are useful in olefin polymerization processes, particularly in the polymerization of predominantly ethylene monomer systems under slurry conditions.

BACKGROUND OF THE INVENTION

This invention relates to silica supported chromium catalysts containing titanium.

Supported chromium oxide catalysts have been used for many years in the polymerization of olefins to solid polymers. One widely used method of producing such catalysts involves precipitating a silica hydrogel, impregnating the hydrogel with an aqueous solution of a chromium compound and drying. Such procedure gives a silica which inherently has sufficient strength to resist severe shrinkage of the pores during simple drying techniques such as oven drying, tray drying, spray drying or drying under a heat lamp. Such catalyst is simple and inexpensive to produce and gives outstanding results in solution polymerization of olefins to give normally solid polymer.

There is an economic advantage in some instances to producing olefin polymers in a slurry as opposed to a solution system. However, certain control operations which are easily carried out in the solution process are considerably more difficult in the particle-form or slurry process. For instance in the solution process, control of the molecular weight can be effected by changing the temperature, with lower molecular weight (higher melt flow) being obtained at the higher temperature. However, in the slurry process, this technique is inherently limited since any effort to increase the melt flow to any appreciable extent by increasing the temperature causes the polymer to go into solution and thus destroys the slurry process.

It is known that titanium affects the polymerization activity of silica supported chromium catalysts in a way that is of special importance in slurry polymerizations. However, when titanium is coprecipitated with the silica, it produces a hydrogel which does not have sufficient strength to resist serious collapse of the pores during simple drying such as spray drying. Accordingly, in order to take full advantage of the improvement which can be imparted to the melt index capability through the use of titanium in accordance with the prior art, the titanium had to be coprecipitated with the silica and the resulting hydrogel (cogel) dried by a more expensive azeotrope distillation or washing with a liquid oxygen-containing water soluble organic compound.

SUMMARY OF THE INVENTION

It is an object of this invention to provide a titanium-containing silica supported chromium catalyst which can be dried in a conventional manner and yet which exhibits the characteristics associated with azeotrope dried titanium-silica coprecipitated catalysts.

It is a further object of this invention to provide a catalyst suitable for use in slurry polymerization systems; and

It is yet a further object of this invention to provide an improved olefin polymerization process.

There are two embodiments to this invention. In accordance with the first embodiment of this invention, a silica xerogel is aqueously impregnated with a titanium compound which is resistant to hydrolysis.

In accordance with the second embodiment of this invention, a silica hydrogel containing a titanium compound resistant to hydrolysis is dried; in this embodiment, the hydrogel preferably also contains a pore preserving agent.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings, forming a part hereof,

FIG. 1 is a plot of melt index versus reoxidation temperature for reduced and reoxidized activated Catalyst A as defined hereinafter which had been aqueously impregnated with 3 weight percent titanium as Tyzor TE, the polymerization temperature being indicated on the graph (Tyzor TE, is a product of E. I. duPont de Nemours & Co., Inc., Wilmington, Del.);

FIG. 2 is a plot of melt index versus air activation temperature for catalyst prepared by aqueously impregnating 952 silica gel with 1 weight percent chromium as chromium (III) acetate (Cr(OAc)₃) and the indicated percentage titanium with Tyzor TE, using a polymerization temperature of 107° C. (952 silica, is a product of Davison Chemical Co.);

FIG. 3 is a plot of melt index versus weight percent titanium for catalyst prepared by aqueously impregnating 952 silica gel with 0.8 weight percent chromium as Cr(OAc)₃ and with the indicated weight percentage titanium as Tyzor TE, the catalyst being air activated at the indicated temperatures (polymerization temperature 107° C.);

FIG. 4 is a plot of melt index versus reoxidation temperature for reduced and reactivated catalysts prepared by aqueously impregnating 952 silica gel with 0.8 weight percent chromium as Cr(OAc)₃ and with the indicated percentage titanium as Tyzor TE (polymerization temperature 104° C., except as indicated where the temperature was 107° C.); and

FIG. 5 is a plot of melt index versus weight percent titanium for reduced and reoxidized activated catalysts prepared by aqueously impregnating 952 silica gel with 0.8 weight percent chromium as Cr(OAc)₃ and with the indicated percentage titanium as Tyzor TE, the catalysts being CO reduced at 871° C. and reoxidized to 538° C. (polymerization temperature 104° C.).

DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment 1

In this embodiment, a dried silica hydrogel (xerogel) is impregnated with an aqueous solution of a hydrolysis resistant titanium compound. In this embodiment, the xerogel can be formed by drying a titanium free hydrogel by conventional means. For instance, an alkali metal silicate can be added to an acid to produce a hydrogel which is washed to remove alkali metal ions, impregnated with an aqueous solution of a chromium compound and thereafter dried in a conventional manner such as spray drying. The silica hydrogel can be prepared in a conventional manner, for instance, by contacting an aqueous acid solution with an aqueous solution of an alkali metal silicate as disclosed in Witt, U.S. Pat. No. 3,900,457, issued Aug. 19, 1975, the disclosure of which is hereby incorporated by reference. Preferably, the alkali metal silicate is added to the acid.

Other conventional drying techniques such as air oven drying, tray drying, vacuum oven drying or drying under a heat lamp or other radiant heat source can be used. Conventional drying temperatures of room temperature to 425° C. or higher can be used to thus remove free water and produce a xerogel. With spray drying the incoming air can be up to 425° C. although the catalyst does not get that hot.

Thereafter, the resulting xerogel is impregnated with an aqueous solution of a hydrolysis resistant titanium compound. A hydrolysis resistant, water soluble titanium compound is required since otherwise titanium precipitates out independently of the silica. When titanium compounds outside the scope of the hydrolysis resistant titanium compounds of this embodiment of this invention are used, polymers made with the resulting catalyst do not exhibit the superior stress crack resistance shown by polymers made through the use of the catalyst of this embodiment of this invention.

The hydrolysis resistant titanium compounds are preferably selected from titanium chelates, particularly alkanolamine titanates, e.g., triethanolamine titanate. The titanium chelates are known compounds and can be expressed by the general formula: ##STR1## where R is an alkyl group containing from 1 to about 4 carbon atoms, A is a functional group containing O or N, or is OH, and B is a divalent hydrocarbon chain of 2 or 3 carbon atoms which can have one or more alkyl groups of 1 to about 4 carbon atoms. An example of a specific compound is triethanolamine titanate chelate. Triethanolamine titanium chelate has the formula ##STR2## This is available from DuPont under the designation Tyzor TE.

Lactic acid titanium complexes such as lactic acid titanium chelates and tetraoctylene glycol titanium complexes such as tetraoctylene glycol titanium chelates are also suitable. A specific example of a lactic acid titanium complexes is: ##STR3## This is available from DuPont under the designation Tyzor LA.

An example of the tetraoctylene glycol titanium complexes is: ##STR4## This is available from DuPont under the designation Tyzor OG.

It must be emphasized that the invention is applicable only to the hydrolysis resistant compounds of the general formula. The three classes of titanium chelates set out hereinabove are hydrolysis resistant. One class, the titanium acetyl acetonates are not and hence cannot be used in this invention. A simple test can be used to determine if a compound is suitable for use in this invention, namely to mix the compound with water. If a precipitate forms, it is not suitable and if no precipitate forms, it is suitable.

The resulting titanium impregnated xerogel can then be activated without further processing expecially if only enough solution is used to just fill the pores. Alternatively, the water can be removed by evaporation at room temperature or an elevated temperature of about 100° to 250° C. or higher prior to the activation.

The activation can be carried out in a conventional manner by calcining at an elevated temperature, generally from about 400° C. to 1100° C. in a dry atmosphere containing oxygen, generally in air. Alternatively, the catalyst can be activated in accordance with the reduction/reoxidation procedures disclosed in McDaniel and Welch, U.S. Pat. No. 4,151,122, which issued Apr. 24, 1979, the disclosure of which is hereby incorporated by reference. Use of this activation technique further enhances the capability to produce high melt index polymers exhibiting superior stress crack resistance.

The final titanium concentration will be such as to give 0.1 to 10 preferably 3-7 weight percent titanium based on the weight of the activated catalyst.

Embodiment 2

In this embodiment, a hydrolysis resistant titanium compound as described in embodiment 1 is incorporated into a hydrogel which is then dried. Conventional techniques as described hereinabove, such as spray drying, oven drying, tray drying, or drying under a heat lamp or other radiant heat source can be used. In this embodiment, it is preferred that the hydrogel further contain a pore preserving agent as described hereinbelow although this is not essential. The resulting titanium-containing xerogel is then activated by calcining as described hereinabove. While the hydrolysis resistant titanium compound can be coprecipitated with the hydrogel, it is preferably added to the hydrogel neat or as a solution in an organic solvent such as isopropanol which is miscible with water. This is because it is normally stored in this form. Alternatively just before using, the hydrolysis resistant titanium compound could be dissolved in water.

The final titanium compound concentration will be such as to give about 0.1 to 10, preferably 2 to 10, more preferably 2-6 percent titanium based on the weight of the activated catalyst.

After the activation step in all of the embodiments, at least a portion of the chromium compound is in the hexavalent state.

In all embodiments, the chromium component of the catalyst can be coprecipitated with the silica or added by means of an anhydrous solution to the xerogel but preferably the chromium is introduced by means of incorporating an aqueous solution of a water soluble chromium compound with the hydrogel. This is preferably done after the hydrogel is washed with water to remove alkali metal ions. The water soluble chromium compound can be selected from among chromium acetate, chromic nitrate, chromic sulfate, chromous sulfate, chromium trioxide, ammonium chromate, and other soluble chromium compounds. Chromium acetate and CrO₃ are preferred.

In all of the embodiments, the amount of chromium compound employed in making the catalyst is sufficient to provide from about 0.001 to about 10 weight percent, preferably 0.1 to 5 weight percent chromium in the final catalyst based on the weight of the activated catalyst.

The silica pore structure preserving agents, when used, can be selected from among organic silicon compounds, e.g., triarylsilanols, described in application Ser. No. 914,258, filed June 9, 1978, the disclosure of which is hereby incorporated by reference; oxygen-containing organic compounds selected from among polyhydric alcohols, mono- and dialkyl ethers of ethylene glycol and poly(alkylene)glycol as disclosed in McDaniel, U.S. Pat. No. 4,169,926, issued Oct. 2, 1979, the disclosure of which is hereby incorporated by reference and surfactants. U.S. Pat. No. 4,169,926 also discloses suitable anionic, cationic and nonionic surfactants. This patent also discloses combinations of the oxygen-containing organic compounds with a normally liquid hydrocarbon, e.g., n-heptane, kerosene, and, optionally, a surfactant, which are also suitable pore preserving agents. The nonionic surfactants are preferred.

The pore preserving agents can also include certain inorganic and organic acids used at a specific level of pH. Specifically the hydrogel is contacted with an inorganic or organic acid in an amount sufficient to impart to the mixture a pH ranging generally from about 0 to about 3.5, more specifically from about 0 to 3. About 2.2 or below is presently preferred.

Inorganic acids employable in this invention are those which are water soluble, sufficiently ionized to produce the pH level required in the hydrogels, and do not have a deleterious effect on the silica or in the end use application. For the production of ethylene polymerization catalysts, specific but nonlimiting acids can be selected from among hydrochloric acid, hydrobromic acid, hydriodic acid, nitric acid, sulfamic acid, sulfuric acid, orthophosphoric acid and iodic acid.

Organic acids generally employable in this invention are those which exhibit the same requirements as the inorganic acids. Specific but nonlimiting examples include acetic acid, formic acid, tartaric acid, citric acid, maleic acid, malic acid, malonic acid, succinic acid, gluconic acid, diglycolic acid, ascorbic acid, cyclopentane tetracarboxylic acid, and benzenesulfonic acid.

In general, those organic acids meeting the requirements of water solubility, stability, acid strength, nondeleterious action as described before also have pK values of about 4.76 or less as disclosed in Lange's Handbook of Chemistry, 11th Edition (1973), Tables 5-7, 5-8. In other words their acid strength is equal to or greater than that of acetic acid.

Acids such as sulfuric acid and hydrochloric acid are generally preferred, however, because of their ready availability, relatively low cost, great acid strength, and efficacy in the process.

The pore preserving agent can be incorporated in one of the ingredients used to make the silica hydrogel, however, it is preferably incorporated into the hydrogel after the washing step since this avoids loss of the agent during the washing step.

When the pore preserving agent is an oxygen-containing organic compound, the weight ratio of oxygen-containing organic compound to hydrogel employed in making the catalyst can range from about 5:1 to about 0.5:1.

When both an oxygen-containing organic compound and a normally liquid hydrocarbon are employed with the hydrogel, the weight ratio of hydrocarbon to organic compound can vary from about 20:1 to about 0.5:1.

When employing one or more surfactants with the hydrocarbon/oxygen-containing organic compound, generally about 0.1 to about 5 weight percent surfactant is used based on the weight of hydrocarbon/oxygen-containing organic compound.

When a surfactant or an organic silicon compound of said Ser. No. 914,258 is employed as the silica pore structure preserving agent, the weight ratio of hydrogel to surfactant or organic silicon compound can range from about 20:1 to about 500:1, preferably from about 40:1 to about 100:1.

Sufficient treating time is allotted to obtain contact of the various added components with the hydrogel or dried gel. Generally, times ranging from about 30 seconds to about 10 hours, preferably 15 minutes to 120 minutes are adequate. The treated hydrogel is then dried as described above to remove the liquids and the composite is then activated at an elevated temperature.

Specific examples of preferred pore preserving agents are a polysiloxane-polyoxyalkylene copolymer, a polyethoxylated sorbitol monolaurate, and a polyethoxylated t-octylphenol.

The catalyst of this invention resembles coprecipitated silica-titania catalyst in pore volume, in chromium content, and in the titanium content although the process for making the catalyst is substantially simplified and substantially less expensive.

The catalyst of this invention can be used to polymerize at least one mono-1-olefin containing 2 to 8 carbon atoms per molecule. The invention is of particular applicability in producing ethylene homopolymers and copolymers from mixtures of ethylene and one or more comonomers selected from 1-olefins containing 3 to 8 carbon atoms per molecule. Exemplary comonomers include aliphatic 1-olefins such as propylene, 1-butene, 1-hexene, and higher 1-olefins and conjugated or nonconjugated diolefins, such as 1,3-butadiene, isoprene, piperylene, 2,3-dimethyl-1,3-butadiene, 1,4-pentadiene, 1,7-hexadiene, and mixtures thereof. Ethylene copolymers preferably constitute at least about 90, more preferably 95 to 99 mole percent polymerized ethylene units. Ethylene, propylene, 1-butene, and 1-hexene are especially preferred.

The polymers can be prepared from the catalyst of this invention by solution polymerization, slurry polymerization, and gas phase polymerization technique using conventional equipment and contacting processes. However, the catalyst of this invention is particularly suitable in slurry polymerizations for the production of high melt index polymers in the absence of molecular weight modifiers, such as hydrogen. The slurry process is generally carried out in an inert diluent such as a paraffin, aromatic or cycloparaffin hydrocarbon. For predominantly ethylene polymers, a temperature of about 66° to 110° C. is employed. Hydrogen or other molecular weight modifiers can be used, of course, if desired. Also conventional cocatalysts and adjuvants and activators can be utilized, if desired.

EXAMPLE I

This exemplifies Embodiment 1 of this invention.

A. Catalyst Preparation:

Aqueously titanated catalysts were prepared in two ways.

1. Aqueous Titanation of Catalyst A

Catalyst A was made by spray drying a silica hydrogel having 20 weight percent solids and containing an aqueous solution of chromium acetate sufficient to give 1 weight percent chromium in the final dried catalyst, said catalyst containing about 0.1 weight percent alumina. To 122 grams of Catalyst A was added 44 g Tyzor TE (DuPont's triethanolamine titanium chelate, 8.3 percent Ti in 150 ml of demineralized water). The resulting dry-appearing catalyst was bottled and labeled reference no. 1-4 for Table I and 1-23 for Table II (when activated, it contained 3 percent Ti, 1 percent Cr by weight).

2. Co-impregnation of Davison 952 Silica Gel with Aqueous Chromium (III) Acetate and Tyzor TE

Aqueous solutions containing the appropriate amounts of chromium acetate and Tyzor TE were prepared at the indicated temperature and diluted with demineralized water to volumes which would be nearly absorbed by the pore structure of weighed amounts of grade 952 silica gel. The solutions were placed in a large evaporating dish and the preweighed silica gel then added, resulting in deep green slurries which were then dried until free flowing by heating the evaporating dish on a large heating mantle. Catalysts prepared in this manner were blue-green in color, and when activated ranged from 0-6 percent Ti, and were about 0.8 percent Cr by weight.

    __________________________________________________________________________     Titanated Catalyst A Preparations                                                  Ref..sup.1                                                                         Wt. Cr                                                                               Tyzor TE.sup.2                                                                       Temp.                                                                              Total Vol.                                                                           Wt. Silica                                                                           Wt..sup.3                                                                          Wt..sup.3                                                                         Wt..sup.4                           Table                                                                              No. (OAc).sub.3 (g)                                                                      (ml)  °C.                                                                         Water (ml)                                                                           gel (g)                                                                              % Cr                                                                               % Ti                                                                              % Ti                                __________________________________________________________________________     III 1-3 5.51  0     R.T.                                                                               600   144   0.87                                                                               0  0                                   IV  1-4                                                                        III 4-6 5.90  18.7  22  516   155   0.86                                                                               1.07                                                                              1                                   IV  5-8                                                                        III 7-9 5.70  54.0  23  500   150   0.84                                                                               2.95                                                                              3                                   IV   9-11                                                                      III 10-12                                                                              7.27  114   19  633   190   0.84                                                                               4.46                                                                              5                                   IV  12-15                                                                      III 13-15                                                                              5.74  126   22  500   150   0.82                                                                               6.26                                                                              7                                   IV  16-18                                                                      __________________________________________________________________________      .sup.1 Catalyst for the indicated runs in the indicated TABLE III or TABL      IV.                                                                            .sup.2 Spec: Gravity = 1.06, 8.3% Ti by weight.                                .sup.3 Determined by analysis.                                                 .sup.4 Calculated values.                                                

B. Catalyst Activations:

Air activated catalysts were heated for five hours under fluidizing conditions (42 std. 1./hr.) at temperatures ranging from 704° to 816° C. Reduction/reoxidation activated-catalysts were heated to 871° C. in an atmosphere of 5% CO in N₂ under fluidizing conditions, held at this temperature for 4 hours, then reduced to the indicated reoxidation temperatures in N₂, and air oxidized for 2 hours.

C. Polymerization Reactions:

Polymerizations were run in a two liter stirred, stainless steel autoclave reactor at 3.89 MPa ethylene using isobutane as a diluent. Reactions were run to 5,000 g/g productivity at temperatures ranging from 99° to 110° C. MI potentials were determined from polymer fluff at 190° C.

D. Results

1. Aqueous Titanation of Catalyst A

Table I contains data comparing the invention Catalyst A to the untitanated Catalyst A under standard air activation conditions. Both catalysts showed the usual increase in MI potential with both increased activation temperature, and increased polymerication temperature. The titanated catalyst however had considerably higher MI potentials under all conditions tested. Shear response was also higher in all cases for polymers prepared from the titanated catalysts. Titanation did not appear to affect activity under these activation and polymerization conditions.

                                      TABLE I                                      __________________________________________________________________________     Air Activated Catalyst A Aqueously Impregnated With 3% Ti as Tyzor             __________________________________________________________________________     TE                                                                             Reference                                                                            Wt. %                                                                              Activation                                                                           Polymerization  HLMI Induction                                                                            Run Time                                                                             Productivity                  Number                                                                               Ti  Temp., C.                                                                            Temp., C.                                                                               MI.sup.1                                                                              MI   Time (min)                                                                           (min.)                                                                               (g/g)  Color                  __________________________________________________________________________     1     3   704   107      0.43 (0.43)                                                                           75   14    77    4920   Orange                 2     3   704   110      1.07 (1.12)                                                                           51   30    87    4800   Orange                 3     3   816   107      0.74 (0.76)                                                                           67   39    72    4830   Green                  4     3   816   110      155 (1.50)                                                                            49   23    83    5180   Green                  5     0   704   107      0.25 (0.25)                                                                           77   33    67    5030   Yellow/Tan             6     0   704   110      0.67 (0.67)                                                                           52   31    83    5010   Yellow/Tan             7     0   816   107      0.48 (0.49)                                                                           68   30    57    4950   Green                  8     0   816   110      1.15 (1.19)                                                                           50   33    64    4820   Green                  __________________________________________________________________________                                            Reference                                                                            Pore Volume                                                                           Surface                                                                             Weight %                                                     Number                                                                               cm.sup.3 /g                                                                           Area                                                                                Cr(VI)2 /g            __________________________________________________________________________                                            1     1.51   290  1.04                                                         2     1.51   290  1.04                                                         3     1.45   263  0.58                                                         4     1.45   263  0.58                                                         5     1.77   308  1.07                                                         6     1.77   308  1.07                                                         7     1.71   282  0.77                                                         8     1.71   282  0.77                  __________________________________________________________________________      .sup.1 Corr. to 5000 g/g prod.                                                  Values in parentheses are uncorrected.                                  

The titanated catalyst responded very well to reduction/reoxidation activation. Table II contains data describing results obtained from a variety of activation and polymerization conditions. All catalysts were CO reduced at 87° C. for 4 hours, and reoxidized at temperatures ranging from 482° to 816° C. Polymerization reactions were run without hydrogen to 5,000 g/g productivity at temperatures ranging from 99° to 107° C. Under these experimental conditions, polymers were produced which ranged in melt index from 8.8 to 0.1. The maximum melt index potential was achieved when reoxidation occurred at 538° C. The MI potential of the reduction/reoxidation activated catalyst dropped off sharply with increased reoxidation temperature (FIG. 1).

All polymers produced by the titanated catalyst had unusually broad molecular weight distributions (indicated by high HLMI/MI ratio when compared to polymers made from Catalyst A.

Catalyst activity was somewhat improved by the presence of titanium. Catalyst samples reoxidized at 649° C. and above had very short induction periods, and reaction times 1 to 5,000 g/g productivity, comparable to or shorter than those of the air activated catalyst A samples.

2. Aqueous Titanation of 952 Silica Gel

                                      TABLE II                                     __________________________________________________________________________     Reduction/Reoxidation Activated Catalyst A Aqueously                           Impregnated with 3% Ti as Tyzor TE                                             __________________________________________________________________________     Reference                                                                            Reoxidation                                                                          Polymerization                                                                               HLMI                                                                               Induction                                                                            Run Time                                                                             Productivity                         Number                                                                               Temp., C.                                                                            Temp., C.                                                                              MI.sup.1                                                                             MI  Time (min)                                                                           (min.)                                                                               (g/g)  Color                         __________________________________________________________________________     1     482   99      1.42 (1.37)                                                                          98  10    79    5190   Green                         2     482   102     2.41 (2.27)                                                                          88  10    89    5300                                 3     482   104.5   4.74 (5.02)                                                                          68  10    130   4730                                 4     482   107     6.71 (7.09)                                                                          58  10    123   4770                                 5     538   99      2.76 (2.46)                                                                          92  39    140   5610   Green/Tan                     6     538   102     3.4 (3.63)                                                                           82  10    80    5390                                 7     538   104.5   5.8 (5.70)                                                                           65  10    120   5290                                 8     538   107     8.8 (8.39)                                                                           61  70    120   5230                                 9     593   102     0.74 (0.67)                                                                          102 49    89    5350                                 10    593   104.5   0.87 (0.81)                                                                          104 10    106   5350   Green/Tan                     11    593   107     1.62 (1.54)                                                                          79  21    90    5250                                 12    649   102     0.79 (0.74)                                                                          96  0     50    5370   Green/Tan                     13    649   104.5   1.29 (1.21)                                                                          87  0     55    5350                                 14    649   107     1.53 (1.62)                                                                          83  10    70    4730                                 15    704   102     0.23 (0.22)                                                                          131 0     70    5300   Yellow/Tan                    16    704   104.5   0.31 (0.31)                                                                          100 3     90    5020                                 17    704   107     0.76 (0.75)                                                                          73  15    60    5090                                 18    760   102     0.12 (0.13)                                                                          153 10    65    4730   Yellow/Tan                    19    760   104.5   0.23 (0.23)                                                                          131 10    49    4970                                 20    760   107     0.59 (0.62)                                                                          75  10    58    4800                                 21    816   102     0.12 (0.14)                                                                          135 14    74    4470   Green                         22    816   104     0.26 (0.26)                                                                          110 10    75    5030                                 23    816   107     0.57 (0.59)                                                                          77  10    59    4810                                 __________________________________________________________________________                                             Reference                                                                            Pore Volume                                                                           Surface                                                                              Wt. %.sup.2                                                 Number                                                                               cm.sup.3 /g                                                                           Area m.sup.2                                                                         Cr(VI)              __________________________________________________________________________                                             1     1.42   255   0.30                                                        2                                                                              3                                                                              4                                                                              5     1.46   268   (0.07)                                                      6                                                                              7                                                                              8                                                                              9     1.44   282   (0.05)                                                      10                                                                             11                                                                             12    1.19   280   0.63                                                        13                                                                             14                                                                             15    1.45   282   0.83                                                        16                                                                             17                                                                             18    1.43   283   0.76                                                        19                                                                             20                                                                             21    1.43   265   0.65                __________________________________________________________________________      .sup.1 Corrected to 5000 g/g productivity, values in parentheses are           uncorrected.                                                                   .sup.2 Values in parentheses are believed to be invalid and have not been      redetermined.                                                            

Table III contains data illustrating the effects of titanium levels on MI potentials of air activated catalysts. FIG. 2 shows that for a given Ti level, MI potentials generally increased with increased activation temperature. It appeared that about 2 percent, preferably 3 percent or more titanium was necessary to achieve substantial MI potential improvements. Titanium levels of 3 to 5 percent resulted in the highest MI potentials at all activation temperatures. FIG. 3 shows that at lower activation temperatures the maximum MI potential is obtained at higher titanium levels. A catalyst containing 5.5 percent Ti activated at 649° C. (1200° F.) was superior in MI potential to the control catalyst activated at 760° C. (1400° F.).

                                      TABLE III                                    __________________________________________________________________________     Air Activated 952 Catalyst Aqueously Impregnated with Cr(OAc).sub.3 and        Tyzor TE                                                                                                       Run             Pore Surface                   Reference                                                                            Wt. %                                                                              Activation  MLMI                                                                               Induction                                                                            Time                                                                               Productivity                                                                               Volume                                                                              Area Wt. %                Number                                                                               Ti  Temp. C.                                                                             MI.sup.1                                                                             MI  Time (min)                                                                           (min.)                                                                             (g/g)  Color                                                                               cm.sup.3 /g                                                                         m.sup.2 /g                                                                          Cr                   __________________________________________________________________________                                                               (VI)                 1     0   649   0.14 (0.14)                                                                          81  48    83  4880   Orange                                                                              1.66 303 0.83                  2     0   760   0.34 (0.32)                                                                          78  38    57  5380   Orange                                                                              1.61 322 0.81                  3     0   871   0.45 (0.45)                                                                          89  20    47  5000   Tan  1.51 285 0.69                  4     1.07                                                                               649   0.19 (0.18)                                                                          71  62    93  5150   Orange                                                                              1.54 271 0.76                  5     1.07                                                                               760   0.30 (0.29)                                                                          78  34    63  5210   Orange                                                                              1.50 297 0.73                  6     11.07                                                                              871   0.36 (0.33)                                                                          101 25    56  5390   Tan/ 1.41 262 0.59                                                             Green                               7     2.95                                                                               649   0.27 (0.26)                                                                          74  62    125 5310   Orange                                                                              1.51 282 0.78                  8     2.95                                                                               760   0.62 (0.58)                                                                          73  35    70  5420   Orange                                                                              1.47 300 0.70                  9     2.95                                                                               871   0.73 (0.71)                                                                          74  41    75  5140   Tan/ 1.33 244 0.61                                                             Yellow                              10    4.46                                                                               649   0.38 (0.38)                                                                          74  10    69  5040   Orange                                                                              1.43 298 0.73                  11    4.46                                                                               760   0.63 (0.71)                                                                          74  10    71  4440   Orange                                                                              1.39 281 0.71                  12    4.46                                                                               871   0.61 (0.56)                                                                          89  10    63  5460   Orange/                                                                             1.27 243 0.61                                                             Yellow                              13    6.26                                                                               649   0.26 (0.28)                                                                          78  12    91  4670   Orange                                                                              1.39 298 0.64                  14    6.26                                                                               760   0.48 (0.50)                                                                          77  10    71  4740   Orange                                                                              1.37 286 0.60                  15    6.26                                                                               871   0.66 (0.67)                                                                          83  15    66  4950   Orange                                                                              1.22 250 0.53                  __________________________________________________________________________      .sup.1 Corrected to 5000 g/g productivity, run at 107° C.               Values in parentheses are uncorrected.                                   

The results of several reduction/reoxidation activations are in Table IV. In FIG. 4, MI potentials are plotted as a function of reoxidation temperature for catalysts containing 0.0 to 6.5 percent Ti by weight. Again maximum MI potentials were achieved at 538° C. reoxidation temperature, however, it did not appear that the MI potential dropped off as sharply with increased reoxidation temperature compared to the titanated finished Type A catalyst (compare FIGS. 1 and 4). FIG. 5 more clearly shows the effect of titanium content on melt index. Increased titanium content dramatically increased MI potentials, MI's as high as 12 were obtained with a 6.5 percent Ti catalyst run at 104° C. without hydrogen. All polymers made from the reduction/reoxidation activated catalysts had higher than usual shear response.

                                      TABLE IV                                     __________________________________________________________________________     Reduction/Reoxidation Activated Catalyst A Aqueously                           Impregnated with Cr(OAc).sub.3 and Tyzor TE                                                                    Run              Pore Surface                  Reference                                                                            Wt. %                                                                              Reoxidation HLMI                                                                               Induction                                                                            Time                                                                               Productivity Volume                                                                              Area Wt. %               Number                                                                               Ti  Temp. C.                                                                             MI.sup.2                                                                             MI  Time (min)                                                                           (min.)                                                                             (g/g)  Color cm.sup.3 /g                                                                         m.sup.2 /g                                                                          Cr(VI)              __________________________________________________________________________     1     0   538   0.94 (0.93)                                                                          67  25    60  5010   Light 1.61 302  0.34                                                           Brown                               2     0   593   0.33 (0.33)                                                                          95  23    70  5050   Tan   --   --   --                  3     0   649   0.37 (0.37)                                                                          106 10    50  5040   Tan   --   --   --                  4     0   704   0.22 (0.21)                                                                          118 13    54  5290   Tan   --   --   --                  5     1.07                                                                               538   1.6 (2.0)                                                                            65  12    58  4280   Tan   1.52 290  0.39                6     1.07                                                                               593   0.75 (0.75)                                                                          86  11    55  5030   Tan   --   --   --                  7     1.07                                                                               649   0.56 (0.51)                                                                          103 10    46  5430   Tan/  1.46 293  --                                                             Orange                              8     1.07                                                                               704   0.30 (0.29)                                                                          114 10    38  5210   Light 1.38 296  --                                                             Orange                              9     2.95                                                                               538   3.77 (4.27)                                                                          63  10    76  4410   Green/                                                                               1.43 280  0.25                                                           tan                                 10    2.95                                                                               593   2.63 (2.59)                                                                          79  10    70  5070   Yellow/                                                                              1.42 285  --                                                             tan                                 11    2.95                                                                               649   1.42 (1.26)                                                                          86  10    53  5640   Yellow                                                                               1.43 284  --                  12    4.46                                                                               538   5.6 (5.16)                                                                           68  10    120 5210   Green 1.31 273  0.20                13    4.46                                                                               593   5.27 (5.18)                                                                          62  22    94  5080   Yellow/                                                                              --   --   --                                                             tan                                 14    4.46                                                                               649   1.88 (1.66)                                                                          97  10    54  5660   Green/                                                                               --   --   --                                                             tan                                 15    4.46                                                                               704   1.96 (2.10)                                                                          87  13    87  4660   Yellow                                                                               --   --   --                  16    6.26                                                                               538   12.0 (15.3)                                                                          51  49    162 3920   Green/                                                                               1.27 286  0.19                                                           yellow                              17    6.26                                                                               593   7.35 (6.7)                                                                           63  10    135 5480   Yellow/                                                                              --   --   --                                                             green                               18    6.26                                                                               649   2.34 (2.35)                                                                          82  70    153 5200   Yellow                                                                               1.26 273  --                  __________________________________________________________________________      .sup.1 Determined by analysis.                                                 .sup.2 Corrected to 5000 g/g productivity. Reactor Temp. 104° C.        Values underlined were run at 107° C.                                   Values in parentheses are uncorrected.                                   

Example II

This demonstrates Embodiment 2 of the invention.

A series of catalysts was prepared from a commercially obtained silica hydrogel containing 20 weight percent solids in the manner described below. In each instance, 100 ml of the hydrogel was admixed with sufficient aqueous chromium trioxide solution to provide 1 weight percent chromium based on the dry composite, a titanium compound, when employed, and 3 volume percent of a liquid surfactant based on the hydrogel, when used. Each mixture was then dried overnight, about 16 hours, in an air oven maintained at 130° C. The dry products of runs 1-5 were individually activated by calcination in a 46 mm diameter quartz tube under fluidizing conditions with dry air at 760° C. for 5 hours. Each recovered sample was stored in a stoppered bottle in a dry atmosphere until ready for further use. The liquid surfactant (except for run 7) was a commercially available organosilicone-based nonionic material sold as L-5340 by the Union Carbide Corp., 270 Park Ave., New York, NY. The surfactant is believed to be a polysiloxane-polyoxyalkylene copolymer.

The nature of each catalyst is further shown below:

Catalyst 1; control, silica containing sufficient chromium compound to give 1 weight percent chromium in the final calcined catalyst with no surfactant or titanium being employed.

Catalyst 2; invention, silica made by adding triethanolamine titanate added to the hydrogel in an amount sufficient to give 1 weight percent titanium in the final calcined catalyst based on the weight of the dry composite with 3 percent surfactant as a pore preserving agent being employed. No reaction with the water was noted with the titanium compound.

Catalyst 3, invention, silica containing sufficient chromium compound to give 1 weight percent chromium, 3 volume percent surfactant added to the hydrogel, and titanium as triethanolamine titanate added to the hydrogel in an amount sufficient to give 4 weight percent titanium in the final catalyst based on the weight of the final calcined catalyst. No reaction of the titanium compound with the water was noted.

Catalyst 4, invention; silica containing sufficient chromium compound to give 1 weight percent chromium in the final catalyst, 3 volume percent surfactant added to the hydrogel, and triethanolamine titanate added to the hydrogel in an amount sufficient to give 6 weight percent titanium in the final catalyst based on the weight of the final calcined catalyst. No reaction with the water was noted with the titanium compound.

Catalyst 5, control; silica containing sufficient chromium compound to give 1 weight percent chromium in the final calcined catalyst, no surfactant used, titanium tetraisopropoxide added to the hydrogel in an amount sufficient to give 4 weight percent titanium based on the weight of the final calcined catalyst. The titanium compound reacted (hydrolyzed) immediately with the water, precipitating titanium dioxide on the silica and container walls.

Catalyst 6, control; silica containing 0.8 weight percent chromium, based on the final calcined catalyst which was produced by impregnating commercially available silica (Davison 952 silica) with an aqueous solution of chromium (III) acetate and drying.

Catalyst 7, invention: To 715 g of a commercially available silica hydrogel containing 28 weight percent solids was added 300 ml of an aqueous solution containing 7.6 g of chromium III acetate, 96 ml of a commercially available nonionic surfactant, a polyethoxylated sorbitol monolaurate, sold by ICI United States Inc., Atlas Chemicals Div., Wilmington, Del., under the trademark Tween 20. The resulting slurry was dried overnight in a vacuum oven. The final calcined catalyst was calculated to contain about 0.8 weight percent Cr and about 4 weight percent Ti.

Catalysts 6 and 7 were individually activated in a fluidized bed by following the procedure detailed below: (a) Heat in 5/95 volume percent CO/nitrogen to 871° C. and hold at that temperature for 4 hours. (b) Reduce temperature to 538° C. in an atmosphere of 100 percent nitrogen. (c) Replace the nitrogen with dry air and hold in dry air at 538° C. for 2 hours, then recover and store in a dry atmosphere until ready for use.

A sample of each activated catalyst was employed in ethylene particle form polymerization at 107° C., unless specified otherwise, using isobutane as diluent as known in the art. A normal reactor pressure of 550 psia (3.9 MPa) was used. Each run was conducted sufficiently long to produce about 5000 g polymer per g catalyst. Each product was recovered at the end of the run by flashing off diluent and ethylene and removing the polymer which was dried and weighed to determine the actual yield. The melt index (MI) and high load melt index (HLMI) was determined for each resin sample in accordance with ASTM Procedure D 1238-65T, Condition E and F, respectively. From the melt index values, the HLMI/MI ratios where calculated to obtain a measure of the molecular weight distribution of the polymer. Each MI value was corrected to a common productivity level of 5000 g polymer per g catalyst so that a valid comparison of the values could be made as is known in the art. The catalyst weights employed and results obtained are given in Table V.

                                      TABLE V                                      __________________________________________________________________________     Ethylene Polymerization, 107° C., 3.9 MPa                               Aqueous Titanation of Hydrogel                                                                              Percent                                                                        Calculated                                        Catalyst   Polymer           Melt Index                                        Run                                                                               Wt. Wt. %                                                                              Yield                                                                               Productivity                                                                            Melt                                                                               Improve-                                                                             HLMI                                        No.                                                                               g   Ti  g    g polymer/g cat.                                                                        Index                                                                              ment  MI  Remarks                                 __________________________________________________________________________     1  0.0460                                                                             0   248  5390     0.34                                                                               --.sup.(a)                                                                           90  control                                 2  .0740                                                                              2   356  4810     0.39                                                                               15.sup.(b)                                                                           79  invention                               3  .0920                                                                              4   405  4400     0.62                                                                               82.sup.(b)                                                                           72  invention                               4  .0715                                                                              6   352  4920     0.63                                                                               85.sup.(b)                                                                           78  invention                               5  .0930                                                                              4.sup.(c)                                                                          dead --       --  --    --  control                                 6.sup.(d)                                                                         .0365                                                                              0   183  5010     0.94                                                                               --    67  control                                 7.sup.(d)                                                                         .0479                                                                              4   240  5010     5.8 517.sup.(e)                                                                          65  invention                               __________________________________________________________________________      .sup.(a) A dash signifies no entry is needed.                                  .sup.(b) Based on melt index of control run 1 for runs 2-4.                    .sup.(c) Based on prior experience, had this catalyst been active; the         melt index of the polymer obtained therewith would be expected to be           similar to that of control run 1.                                              .sup.(d) Reactor temperature was 104° C.                                .sup.(e) Based on melt index of control run 6 for run 7.                 

The results presented in Table V in invention runs 2-4 show that triethanolamine titanate can be added to a silica hydrogel containing a water soluble chromium compound plus a nonionic surfactant, the mixture can be dried in an air oven and the product can be conventionally activated with dry air or sequentially in CO/N₂, then dry air, at an elevated temperature to produce active ethylene polymerization catalysts having enhanced melt index capability compared to control catalysts. The results suggest that a titanium level, calculated as the metal, of about 4 weight percent is sufficient to improve the melt index capability of silica-chromium oxide catalyst as exemplified in control run 1 by at least about 80 percent. A higher titanium level affords little improvement in melt index capability, a lower level, specifically 2 weight percent titanium, gives a catalyst having about a 15 percent improvement in melt index capability.

The poor results of control run 5 utilizing a catalyst containing titanium derived from a water sensitive titanium compound (titanium tetraisopropoxide) shows that titanation of silica hydrogels requires a hydrolysis-resistant titanium compound if an active polymerization catalyst is desired. Otherwise, the precipitated titania forms a mixture with the silica that at best is no better than silica alone as a component of the silica-chromium oxide catalyst.

The fractional melt index polymers produced with invention catalysts 2-4 as prepared in this example are expected to be of value in blow molding, extrusion, etc. since the articles would have good environmental stress cracking resistance. Copolymerizing a minor amount of 1-butene or 1-hexene with the ethylene, e.g., about 10 mole percent, in the presence of the catalysts would yield fractional melt index copolymers having even better stress cracking resistance than the homopolymers.

Invention catalyst 7 demonstrates that relatively high melt index ethylene polymers can be produced when the catalyst is activated sequentially in a carbon monoxide ambient then an air ambient. About a five-fold increase (517 percent) in melt index capability over control catalyst 6 is shown. The results also demonstrate in run 7 that the nonionic surfactant employed is equivalent to the silicone based surfactant employed in runs 2-4, in producing active catalysts.

While this invention has been described in detail for the purpose of illustration, it is not to be construed as limited thereby but is intended to cover all changes and modifications within the spirit and scope thereof. 

I claim:
 1. A process for producing a chromium-containing catalyst comprising impregnating a dry silica xerogel, formed by drying a silica hydrogel, with an aqueous solution of a hydrolysis resistant titanium compound.
 2. A method according to claim 1 wherein said silica is made by adding an alkali metal silicate to an acid to form a hydrogel, washing the hydrogel with water, impregnating the thus washed hydrogel with an aqueous solution of a chromium compound selected from CrO₃ and chromium acetate and spray drying.
 3. A method according to claim 2 wherein said hydrolysis resistant titanium compound is a titanium chelate having the formula ##STR5## where R is an alkyl group containing from 1 to about 4 carbon atoms, A is a functional group containing O or N or is OH, and B is a divalent hydrocarbon chain of 2 or 3 carbon atoms which can have one or more alkyl groups of 1 to about 4 carbon atoms.
 4. A method according to claim 3 where said hydrolysis resistant titanium compound is lactic acid titanium chelate.
 5. A method according to claim 3 wherein said hydrolysis resistant compound is tetraoctylene glycol titanium chelate.
 6. A method according to claim 3 wherein said hydrolysis resistant titanium compound is triethanolamine titanate.
 7. A method according to claim 3 wherein said dried hydrogel containing said titanium compound is activated by reduction and reoxidation.
 8. A method according to claim 6 wherein the titanium-impregnated chromium-containing catalyst is dried and thereafter activated in air at a temperature within the range of 400° to 1100° C., and wherein said catalyst contains from about 0.5 to about 4 weight percent chromium and 2 to 6 weight percent titanium based on the weight of the activated catalyst.
 9. A catalyst produced by the method of claim
 8. 10. A catalyst produced by the method of claim
 1. 11. A process for preparing a chromium-containing catalyst comprising forming a silica hydrogel containing a hydrolysis resistant titanium compound, and drying said hydrogel to form a xerogel.
 12. A method according to claim 11 wherein said chromium is added as an aqueous solution to said hydrogel.
 13. A method according to claim 12 wherein said chromium is in the form of a compound selected from CrO₃ and chromium acetate.
 14. A method according to claim 13 wherein said hydrogel is formed by adding an alkali metal silicate to an acid.
 15. A method according to claim 14 wherein said hydrogel is spray dried and said hydrolysis resistant titanium compound is incorporated into said hydrogel by adding it to the hydrogel after the hydrogel is formed.
 16. A method according to claim 15 wherein said hydrolysis resistant titanium compound is a titanium chelate having the formula ##STR6## where R is an alkyl group containing from 1 to about 4 carbon atoms, A is a functional group containing O or N or is OH, and B is a divalent hydrocarbon chain of 2 or 3 carbon atoms which can have one or more alkyl groups of 1 to about 4 carbon atoms.
 17. A method according to claim 16 wherein said hydrolysis resistant titanium compound is triethanolamine titanate.
 18. A method according to claim 16 wherein said hydrolysis resistant titanium chelate compound is lactic acid titanium chelate.
 19. A method according to claim 16 wherein said hydrolysis resistant titanium compound is tetraoctylene glycol titanium chelate.
 20. A method according to claim 16 wherein said xerogel is activated by reduction and reoxidation.
 21. A method according to claim 17 wherein said thus spray dried catalyst is activated in air at a temperature within the range of 400° to 1100° C. and wherein the thus-activated catalyst contains chromium in an amount within the range of 0.5 to 4 weight percent and titanium and an amount within the range of 2 to 6 weight percent based on the weight of the activated catalyst.
 22. A catalyst produced by the method of claim
 21. 23. A catalyst produced by the method of claim
 11. 24. A process according to claim 11 wherein said hydrogel contains in addition a pore preserving agent selected from organic silicon compounds, oxygen-containing organic compounds, acids, and surfactants.
 25. A method according to claim 24 wherein said hydrogel is washed with water and subsequent to said washing said pore preserving agent is added to the thus-washed hydrogel.
 26. A method according to claim 25 wherein said chromium is added as an aqueous solution to said hydrogel.
 27. A method according to claim 26 wherein said chromium is in the form of a compound selected from CrO₃ and chromium acetate.
 28. A method according to claim 27 wherein said hydrogel is formed by adding an alkali metal silicate to an acid.
 29. A method according to claim 28 wherein said hydrogel is dried by spray drying.
 30. A method according to claim 29 wherein said hydrolysis resistant titanium compound is selected from a titanium chelate having the formula ##STR7## wherein R is an alkyl group containing from 1 to about 4 carbon atoms, A is a functional group containing O or N or is OH, and B is a divalent hydrocarbon chain of 2 or 3 carbon atoms which can have one or more alkyl groups of 1 to about 4 carbon atoms.
 31. A method according to claim 30 wherein said hydrolysis resistant titanium compound is triethanolamine titanate.
 32. A method according to claim 30 wherein said hydrolysis resistant titanium compound is triethanolamine titanate.
 33. A method according to claim 30 wherein said hydrolysis resistant titanium compound is lactic acid titanium chelate.
 34. A method according to claim 30 wherein said hydrolysis resistant titanium compound is tetraoctylene glycol titanium chelate.
 35. A method according to claim 30 wherein said xerogel is activated by reduction and reoxidation.
 36. A method according to claim 32 wherein said pore preserving agent is selected from a polysiloxane-polyoxyalkylene copolymer, a polyethoxylated sorbitol monolaurate, a polyethoxylated t-octylphenol.
 37. A catalyst produced by the method of claim
 36. 38. A catalyst produced by the method of claim
 24. 